A little while back I went to have my aluminum wheels powdercoated, and the guy at the local place advised me not to since they were aluminum. He said that the heat from the oven could make them fracture under pressure
Anyone know if this is true?
If it's not true, than powdercoating would definitely worth it. But if it puts the wheels at risk, then idk